[交流]
超聲自組裝納米粒子，超聲波的參數(shù)一般為多少��？
|
||
回復(fù)此樓
送紅花一朵 3樓2020-01-15 14:57:15
2樓2020-01-15 12:01:57
★
小木蟲: 金幣+0.5, 給個紅包，謝謝回帖
小木蟲: 金幣+0.5, 給個紅包，謝謝回帖
|
10 mg copolymer was dissolved in 1 mL dichloromethane to a form copolymer solution. 10 mL aqueous solution was added to the copolymer solution and emulsified using sonication for 3 min (30 W) to get a W1/O emulsion. 2 mL 2% (w/v) PVA aqueous solution W2 was then added and sonicated for 5 min (80 W) to make a W1/O/W2 emulsion. The resulting W1/O/W2 emulsion was then diluted into 10 mL 0.3% (w/v) PVA solution and the dichloromethane was removed by evaporation under reduced pressure. The obtained NPs were collected by centrifugation at 13 000 rpm for 15 min and then washed three times with distilled water. ——Nie X, Zhang J, Xu Q, et al. Targeting peptide iRGD-conjugated amphiphilic chitosan-co-PLA/DPPE drug delivery system for enhanced tumor therapy[J]. Journal of Materials Chemistry B, 2014, 2(21): 3232-3242. |
4樓2020-01-16 21:15:59
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[碩博家園] 售SCI一區(qū)T0P文章，我:8.O.5.5.1.O.5.4 +3 | 7mzg0e04z2 2026-03-06 | 5/250 |
|
|---|---|---|---|---|
|
|
[考博] 售瀆SCI文章，我:8⊙ 55 1⊙ 54。備注【⊙=0】 +4 | vs9ky3szrj 2026-03-06 | 5/250 |
|
|
|
[考研] 物理學(xué)求調(diào)劑 +3 | sx宋 2026-03-05 | 3/150 |
|
|
|
[基金申請]
 成果系統(tǒng)訪問量大，請15分鐘后再嘗試。由此給您造成的不便，敬請諒解。
+16
|
xhuama 2026-03-02 | 18/900 |
|
|
[考研] 一志愿中石油，化學(xué)工程，301求調(diào)劑 +4 | 豚饅枳枳 2026-03-04 | 4/200 |
|
|
|
[考研] 材料調(diào)劑 +5 | ounce. 2026-03-05 | 13/650 |
|
|
|
[考研] 哈爾濱理工大學(xué)2026年研究生調(diào)劑，材料科學(xué)與化學(xué)工程學(xué)院研究生調(diào)劑 +3 | xinliu866 2026-03-06 | 3/150 |
|
|
|
[考研] 085600材料與化工（高分子）290分求調(diào)劑 +9 | wengyujian 2026-03-04 | 9/450 |
|
|
|
[考研] 085602高分子方向求調(diào)劑 +7 | tlgudy 2026-03-04 | 7/350 |
|
|
|
[考研] 289求調(diào)劑 +3 | 馳光絕景 2026-03-04 | 4/200 |
|
|
|
[考研] 一志愿蘇大材料工程專碩293求調(diào)劑 +3 | 鋼鐵大炮 2026-03-04 | 3/150 |
|
|
|
[考研] 301求調(diào)劑 +4 | 李LJR 2026-03-04 | 4/200 |
|
|
|
[考研] 304分材料專碩求調(diào)劑 +11 | qiuzhigril 2026-03-03 | 14/700 |
|
|
|
[考研] 化學(xué)工程求調(diào)劑 +10 | 化工人999 2026-03-04 | 10/500 |
|
|
|
[考研] 求調(diào)劑 +7 | 博斯特525 2026-03-04 | 7/350 |
|
|
|
[考研] 材料專碩346求調(diào)劑 +3 | 旺一下 2026-03-04 | 3/150 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 +4 | G212 2026-03-03 | 5/250 |
|
|
|
[考研] 清華大學(xué) 材料與化工 353分求調(diào)劑 +5 | awaystay 2026-03-02 | 6/300 |
|
|
|
[考研] 一志愿鄭大材料學(xué)碩298分，求調(diào)劑 +6 | wsl111 2026-03-01 | 6/300 |
|
|
|
[考研] 295復(fù)試調(diào)劑 +3 | 簡木ChuFront 2026-03-01 | 3/150 |
|